Method and installation for the production of steel products having an optimum surface quality

ABSTRACT

Disclosed are a method and an installation for producing steel products ( 1 ) having an optimum surface quality, especially extremely low carbon contents (UCL steel or IF steel), nitrogen contents, total oxygen contents, high-strength or stainless steel qualities. According to the invention, the liquid steel is cast into a thin slab ( 5   a ) from a process route ( 10, 11, 12 , or  13 ) that is selected according to the desired final structure ( 9 ) based on an electric-arc furnace ( 2   b ), is descaled, cut into billets ( 15 ) having a partial length, optionally descaled once again, subjected to final descaling downstream from a holding furnace ( 16 ), milled in a finishing mill train ( 6   a ), rolled up in a rolling station ( 20 ) located downstream from the last finishing mill stand ( 19 ) or downstream from a cooling section ( 21 ), and the final structure ( 9 ) is adjusted in the cooling section ( 21 ) according to the desired steel quality by cooling on a run-out roller table ( 22 ), whereupon the rolling stock ( 1   a ) is completely rolled up in a second rolling station ( 23 ).

This application is a 371 of PCT/EP04/05580 filed May 25, 2004.

The invention concerns a method and an installation for producing steel products with optimum surface quality, especially with ultralow carbon contents (ULC or IF steel), nitrogen contents, total oxygen contents, and high-strength or stainless steel grades, in each case by melting, treatment in a ladle metallurgy installation, continuous casting in slab format, rolling, cooling, and usually coiling of the rolled product.

Steel products of this type in various steel grades have previously been produced by melting in a converter, treatment in the ladle metallurgy installation with vacuum degassing, and casting as thick slabs in a continuous casting machine, and then rolled in roughing mills and finishing mills. Production by means of other process routes, e.g., the electric arc furnace process from scrap, was not considered possible, because then the extremely low contents of such elements as C, N, S, O, <O>, and quality-reducing trace elements, e.g., Cu and Zn, cannot be achieved or can be achieved only under difficult conditions. These process routes do not allow the optimum surface quality that is being strived for to be achieved. There is a lack, for example, of the required geometric, physical, and structural product properties of ULC and IF hot rolled strip that are necessary prerequisites for effective microstructural control and systematic adjustment of product properties.

The objective of the invention is to produce the specified steel grades and other steel grades by new process routes in order to achieve the required ultralow contents of C, N, S, O, <O>, and quality-reducing trace elements, e.g., Cu and Zn, for steel products with optimum surface quality.

In accordance with the invention, this objective is achieved by a method that is characterized by the fact that molten steel is produced in a process route which is based on an electric arc furnace and which is selected according to the desired final microstructure; by the fact that the molten steel from the selected process route is then cast into a thin slab in the continuous casting mold; by the fact that the thin slab is descaled, partially deformed, cut to partial lengths, generally descaled, heated to rolling temperature and homogenized in a soaking furnace, generally descaled again, and rolled in a finishing mill; by the fact that the rolled product is coiled in a first coiling station immediately downstream of the last finishing stand or, alternatively, downstream of a cooling line; by the fact that the final microstructure is adjusted in a cooling line according to the desired grade of steel by cooling on a runout table; and by the fact that the rolled product is generally finish-coiled in a second coiling station. In this way, the steel products can be produced downstream of the ladle metallurgy installation on the basis of thin slabs and finished as coiled strip, sections of strip, or other flat products and possibly long products with high surface quality and a very exact final microstructure.

In accordance with additional steps, steel products of this type, whose final microstructure can be more exactly controlled, can be produced in different process routes. In accordance with a first alternative, it is proposed that successive treatment steps be carried out as a first process route

-   -   in an electric arc furnace and     -   in a ladle metallurgy installation         -   with at least one vacuum degassing system followed by a             ladle furnace for decarbonization, reduction, and addition             of alloying materials,         -   with a ladle furnace for slag formation, for slag work, for             temperature control, for final adjustment of the final             analysis, and for purity rinsing to Δ <Al> contents.

The advantage consists in the final microstructure of the aforementioned ULC, IF, high-strength and stainless steel grades, which, after a vacuum treatment, has values of <20 ppm to 30 ppm for C, <3 ppm for O, <15 ppm for <O>, 20-30 ppm for N, and

<100 ppm for S. The steel that is cast in the continuous casting machine has these values.

After being tapped from the electric arc furnace, the steel has the following values before the vacuum treatment is carried out: C=400-600 ppm, S<150 ppm, N<35 ppm, and oxygen-free <600 ppm. After the degassing treatment, these values fall to C<15 ppm, S<150 ppm, N<35 ppm, and O<3 ppm. The advantages are moderate foaming during slag formation (assuming 100% DRI), slag-free tapping, the possible slag additives, and prereduction by FeMnHC.

After the ladle furnace treatment, these values can be further altered for the casting operation in the continuous casting machine to C<25 ppm, S<50 ppm, N<35 ppm, O<3 ppm and <O><15 ppm.

During the vacuum treatment of the steel by the partial-quantity method, basically a decarbonization, a deoxidation, and an addition of ferroalloys is undertaken. The necessary refining of the ladle slag, the desulfurization, and the final adjustment of the chemical analysis of the molten steel occur during the ladle furnace treatment, which is concluded by a purity treatment.

During the addition of slag additives, slag work in the steel, a heating operation, the desulfurization, and an adjustment of the final analysis, another purity rinsing is carried out, which considerably increases the preciseness of the final grade. Before the molten steel is cast, the following values can be adjusted: C<25 ppm, S<50 ppm, N<35 ppm, O<3 ppm and <O><15 ppm.

In accordance with a second alternative, it is proposed that successive treatment steps be carried out as a second process route

-   -   in an electric arc furnace or an electric arc furnace         installation and     -   in a ladle metallurgy installation         -   with a ladle furnace for slag formation,             -   for the heating             -   and for the prereduction (FeMnHC) of the steel         -   with a vacuum degassing system             -   for the decarbonization and denitrogenation             -   for the reduction of the slag on the steel surface             -   for the desulfurization under reduced pressure,             -   for the final adjustment of the final analysis and             -   for the purity rinsing to Δ <Al> under atmospheric                 pressure.

The advantages are that it is also possible to charge up to 100% DRI or pig iron or hot metal and scrap in any desired proportions. Slag-free deslagging can then be carried out. Additional slag is produced during the ladle furnace treatment; the total ladle slag reaches about 8 kg/t. Heating and adjustment of the reduction slag (with FeMnHC) are then carried out. During the treatment in the vacuum degassing system, a decarbonization, a reduction and slag work, a desulfurization and a denitrogenation under reduced pressure, an adjustment of the final analysis, and stirring for the degree of purity under atmospheric pressure are carried out.

In accordance with a third alternative, it is proposed that successive treatment steps be carried out as a third process route

-   -   in an electric arc furnace or in an electric arc furnace         installation and     -   in a ladle metallurgy installation         -   with a ladle furnace             -   for temperature control and             -   for prereduction (FeMnHC)         -   with at least one differential-pressure degassing process             for the decarbonization, desulfurization (under pressure)             and denitrogenation, reduction, and addition of alloying             materials from an iron alloy, and with final adjustment             -   of the final analysis and             -   for the purity rinsing to <Al> contents of <15 ppm bound                 aluminum <Al₂O₃> or <O> of <15 ppm under atmospheric                 pressure.

The advantages are that the molten steel attains the following values in the electric arc furnace:

C 500-800 ppm;

O 500-700 ppm;

N 60-100 ppm;

S 160-300 ppm.

The following values are then attained in the vacuum degassing system:

C<40 ppm;

O<3 ppm;

N<40 ppm;

S<50 ppm;

<Al><15 ppm.

The steel is cast with the following values in the downstream CSP continuous casting machine:

C<50 ppm;

O<3 ppm;

N<40 ppm;

S<50 ppm;

<Al><15 ppm.

In accordance with a fourth alternative, it is proposed that successive treatment steps be carried out as a fourth process route

-   -   in an electric arc furnace or in an electric arc furnace         installation and     -   in a ladle metallurgy installation         -   with a ladle furnace for temperature control and a             subsequent partial-quantity degassing for decarbonization             and denitrogenation, desulfurization, with a ladle degassing             for the final adjustment of the final analysis and for             purity rinsing to Δ <Al> contents.

The advantages are likewise the attainment of very low values of the companion elements for casting in the thin-slab continuous casting machine and the adjustment of the final microstructure.

In one embodiment, a descaling is carried out directly below the continuous casting mold. The purpose of this step is preparation for ensuring optimum surface quality by controlling the scaling processes in the continuous casting machine, wherein special methods of descaling can be used.

Another step in this direction consists in undertaking controlled high-temperature oxidation by a controlled atmosphere in the soaking furnace.

This purpose is assisted by the additional feature of inductive heating of the partial strand lengths downstream of the soaking furnace. In this way, the heating can be transferred to the partial length of strand systematically, uniformly, and very quickly.

The most favorable temperature level is then reached by controlled cooling of the partial strand lengths before the first finishing stand of the finishing mill.

In another step, the final microstructure can be systematically adjusted by controlled cooling of continuous product coiled in the second coiling station.

Another improvement consists in using an electric arc furnace installation with two furnace vessels, which are alternately operated with a swiveled electrode system and an oppositely swiveled top injection lance, are operated with pig iron, direct reduced charge materials, and scrap, and are operated partially with electric power and/or chemical energy (so-called CONARC® processes).

The method can be applied in such a way that steels with multiphase microstructure (dual-phase steel or TRIP steel) are produced.

The installation for producing steel products with optimum surface quality, especially with ultralow carbon contents (ULC or IF steel), nitrogen contents, total oxygen contents, high-strength and/or stainless steel grades, is based on a prior art using at least a melting installation, a ladle metallurgy installation, a continuous casting machine for slab strands, a rolling mill, a runout table, and a coiling station.

In accordance with the invention, the stated objective is achieved by using a melting installation, which consists of an electric arc furnace installation, with a ladle metallurgy installation that is downstream with respect to the material flow by providing the continuous casting machine with a continuous casting mold in thin-slab format, and by providing in the material flow at least one descaling system, a shear, a soaking furnace, a finishing mill, and at least one rollout table with a cooling line upstream or downstream of a coiling station. In this way, all advantages are achieved for a desired final microstructure of hot strip, long products, and the like, which are necessary for ULC, IF, high-strength, or stainless steels.

A feature that is aimed especially at achieving optimum surface quality of the finished steel product consists in providing a descaling system in the continuous casting machine directly below the continuous casting mold.

The quality of the surface of the steel product can be further ensured by providing a descaling system not only downstream of the continuous casting mold and downstream of the shear but also upstream of the first rolling stand of the finishing mill.

In another embodiment, a liquid core reduction line or a soft reduction line is arranged upstream of the shear in the containment roll stand of the continuous casting machine.

In another measure for creating favorable conditions for the final processing of the steel product, the continuous casting mold is designed as a continuous casting mold with a pouring gate.

In accordance with a further improvement, the rolled product is heated in an advantageous way by providing an inductive heating installation in the material flow between the soaking furnace and the first rolling stand of the finishing mill or the descaling system.

Another embodiment provides that the cooling line comprises a laminar cooling line combined with several intensive cooling boxes.

The drawings show specific embodiments of the installation, and the method is described in greater detail below with reference to these drawings.

FIG. 1 shows functional block diagrams of process routes, which are alternatively arranged upstream of a continuous casting and rolling installation.

FIG. 2A shows process routes 1 and 2 in an enlarged view.

FIG. 2B shows process routes 3 and 4 in an enlarged view.

FIG. 3 shows the continuous casting and rolling installation with final microstructure adjustment downstream of the melting and ladle metallurgy installation.

FIG. 4 shows a time-temperature-transformation diagram for cooling microstructure (austenitic, soft pearlite, bainite, and martensite) obtained after the last rolling stand of the finishing mill by cooling of the rolled product.

FIG. 5 shows a strength-strain diagram for multiphase steel grades (dual-phase steels, TRIP-phase steels).

In accordance with FIG. 1 and FIGS. 2A and 2B, the steel product 1 can be produced as hot strip for further processing (e.g., automobile skin sheet, sheet for welded pipes, and the like.)

The liquid steel 1 b is produced by melting 2 in a melting installation 2 a, which is not a steelworks converter but rather an electric arc furnace 2 b. The tapped steel then passes through a ladle metallurgy installation 3 and a continuous casting process 4 with a continuous casting machine 4 a. However, the slab format 5 that is cast there is not a thick slab but rather a thin slab 5 a with customary thicknesses of <100 mm. Rolling 6 is then carried out in a finishing mill 6 a. The rolling stock 1 a in the form of continuous product 1 c (sheet, strip, long products, and the like) is subjected to controlled cooling on a rollout table 22. The cooling 7 is carried out on the basis of important criteria that will be described later. Apart from certain exceptions, the continuous product 1 c with a final microstructure 9 is generally coiled 8 in coiling stations.

The melting installation 2 a consists in each case of the electric arc furnace 2 b, which can also be a two-vessel electric arc furnace installation 35 of the CONARC® type. Steel with the desired extremely low carbon contents (ULC steel=ultralow carbon steel), steel with controlled precipitates (IF steel=steel without interstitially dissolved foreign atoms in the solid solution), and high-strength and/or stainless steel is prepared in the following ladle metallurgy installation 3.

The liquid steel 1 b is cast in thin-slab format in the continuous casting machine 4 a by means of a continuous casting mold 14. The material flow 36 includes at least one descaling system 28 a for descaling 28, a shear 38 for producing partial lengths 15, a soaking furnace 16 (an additional soaking furnace 16 a), the finishing mill 6 a, and at least one runout table 22 with a cooling line 21 upstream or downstream of a first coiling station 20.

A first descaling system 28 a, which is based on water jets, is provided in the continuous casting machine 4 a for descaling 28 directly below the continuous casting mold 14.

In addition to this descaling system 28 a, additional descaling systems 28 a are located in the material flow 36 downstream of the continuous casting mold 14, downstream of the shear 38, and upstream of the first rolling stand 17 of the finishing mill 6 a. Temperature control with oxidation protection 37 is provided in the soaking furnace 16 (possibly in 16 a).

A liquid core reduction line 40 or a soft reduction line can be used upstream of the shear 38 in a containment roll stand 39 of the continuous casting machine 4 a.

The continuous casting mold 14 can be a gate continuous casting mold, as is usually provided in CSP installations.

An inductive heating installation 42 can be arranged in the material flow 36 between the soaking furnace 16 and the first finishing stand 17, which is followed by several finishing stands 18 and a last finishing stand 19, or between the soaking furnace 16 and the descaling system 28 a.

In addition, the cooling line 21 can comprise a laminar cooling line 21 a combined with several intensive cooling boxes 21 b.

The method for producing steel products 1 (FIG. 1) is characterized by the fact that the molten steel 1 b is pretreated by alternative process routes 10, 11, 12, or 13 and cast into a thin slab 5 a in the continuous casting mold 14; by the fact that the thin slab is descaled, possibly partially deformed, cut to partial lengths 15, subjected to repeated descaling 28, heated to rolling temperature, and homogenized in at least one soaking furnace 16 (or an additional soaking furnace 16 a), generally (apart from a few exceptions) descaled again, and rolled in the finishing mill 6 a; by the fact that the rolled product is coiled in a first coiling station 20 immediately downstream of the last finishing stand 19 or, alternatively, downstream of the cooling line 21; by the fact that the final microstructure 9 is adjusted in the cooling line 21 according to the desired grade of steel by cooling on the runout table 22; and by the fact that the rolled product 1 a is generally finish-coiled in a second coiling station 23.

While the first to fourth process routes 10, 11, 12, and 13 in FIG. 1 have been explained only as a group, the process routes in FIGS. 2A and 2B will be individually explained in detail.

The first process route 10 (FIG. 2A) provides for charge materials from DRI/HBI (pellets or briquets of direct reduced iron) or scrap in the electric arc furnace 2 b with extremely low input sulfur contents. In the next treatment step 24, reduction of carbon and oxygen to extremely low values occurs in the process of partial-quantity degassing 27 a within the vacuum degassing system 27. In the following treatment step 24, the temperature is increased by ΔT in the ladle furnace 25, and the degree of purity is adjusted by reduction of the <Al> content.

The second process route 11 (FIG. 2B) starts with the charging of DRI/HBI, scrap, hot metal, or pig iron, each with a low sulfur content, into an electric arc furnace installation 35. The electric arc furnace installation 35 can consist of either an electric arc furnace 2 b or an installation for the CONARC® process. The next treatment step 24 takes place in the ladle furnace 25 with a temperature increase. In the following treatment step 24, a decarbonization, a desulfurization, a denitrogenation, and an increase in the degree of purity by reduction of the <Al> content to low values are carried out in the vacuum degassing system 27.

The third process route 12 (FIG. 2B) provides for the charging of DRI/HBI, scrap, hot metal, or pig iron, each with low input sulfur contents, into an electric arc furnace installation 35 or into an electric arc furnace 2 b. In the following treatment step 24, a temperature increase ΔT takes place in the ladle furnace 25. In the next treatment step 24, differential-pressure vacuum degassing 43 is provided, in which carbon C, sulfur S and nitrogen N are reduced to very low values, and the degree of purity is increased by decomposition of the Al₂O₃ materials (Δ <Al>)

The fourth process route 13 (FIG. 2B) provides for the charging of DRI/HBI, scrap, hot metal, or pig iron, each with a low sulfur input content, into an electric arc furnace installation 35 or into an individual electric arc furnace 2 b. In the next treatment step 24, a temperature increase ΔT takes place in the ladle furnace 25, which is immediately followed by a partial-quantity degassing 27 a in the vacuum degassing system 27, which reduces carbon C and nitrogen N to very low values. In the last treatment step 24, a ladle degassing is carried out in the vacuum degassing system 27 to reduce sulfur S to low values and to increase the degree of purity by the decomposition of Al₂O₃ (Δ <Al>).

The most favorable or desired process route 10, 11, 12, or 13 is selected on the basis of economic considerations with respect to the costs of the charge material and the quality of the final product. The casting of thick or thin slabs, the energy sources to be used, and the required capital investments for the plant are also to be considered.

After the entry (FIG. 3) of the treated steel 1 b, descaling 28 is carried out below the continuous casting mold 14.

Controlled high-temperature oxidation 29 by a controlled atmosphere is carried out in the soaking furnace 16.

In addition, the partial strand lengths 15 can be inductively heated downstream of the soaking furnace 16. Furthermore, an additional soaking heat treatment can be carried out in an additional soaking furnace 16 a following the inductive heating installation 42. The partial strand lengths 15 are further inductively heated in the inductive heating installation 42 downstream of the soaking furnace 16. The ladle furnace 25 operates with an electrode system 31 and/or a top injection lance 32.

After the first finishing stand 17 and between the finishing stands 18, 19 of the finishing mill 6 a, the partial lengths 15 can be subjected to controlled cooling. To this end, intensive cooling boxes 21 b can be arranged between the finishing stands 17, 18, 19. An edger 44 can be positioned in front of the first finishing stand 17.

The coiled continuous product 1 c is subjected to controlled cooling in the second coiling station 23.

The multiphase microstructure is adjusted in the cooling line 21 or in the coil 23.

FIG. 4 shows a schematic temperature curve in a time-temperature-transformation diagram. The cooling curve of the solid material after the last rolling stand 19 during the coiling of the rolled product 1 a in the second coiling station 23 passes through the transformation point AC3. The resulting final microstructure 9 can be austenite, soft pearlite, bainite, or martensite. The final structure 9 is thus produced during the rolling and cooling.

FIG. 5 shows a diagram of strength (N/mm²) versus strain (I/I₀) for multiphase steel, e.g., dual-phase steel 33 and TRIP steel 34. The bottom curve shows normal behavior of steel at high strength and low strain.

LIST OF REFERENCE NUMBERS

-   1 steel product -   1 a rolled product -   1 b liquid steel -   1 c continuous product -   2 melting -   2 a melting installation -   2 b electric arc furnace -   3 ladle metallurgy installation -   4 continuous casting -   4 a continuous casting machine -   5 slab format -   5 a thin slab -   6 rolling -   6 a finishing mill -   7 cooling -   8 coiling -   9 final microstructure -   10 first process route -   11 second process route -   12 third process route -   13 fourth process route -   14 continuous casting mold -   15 partial length of strand -   16 soaking furnace -   16 a additional soaking furnace -   17 first finishing stand -   18 finishing stand -   19 last finishing stand -   20 coiling station (carousel coiler) -   21 cooling line -   21 a laminar cooling line -   21 b intensive cooling boxes -   22 runout table -   23 coiling station -   23 a controlled cooling device for coils -   24 treatment steps -   25 ladle furnace -   26 alloying materials -   27 vacuum degassing system -   27 a partial-quantity degassing -   28 descaling -   28 a descaling system -   29 controlled high-temperature oxidation -   30 furnace vessel (converter or electric arc furnace) -   31 electrode system -   32 top injection lance -   33 dual-phase steel -   34 TRIP steel -   35 electric arc furnace installation -   36 material flow -   37 controlled cooling and oxidation protection -   38 shear -   39 containment roll stand -   40 liquid core reduction line -   41 soft reduction line -   42 inductive heating installation -   43 differential-pressure vacuum degassing system -   44 edger 

1. Method for producing steel products (1) with optimum surface quality of an ultralow carbon, high-strength and/or stainless steel grade, comprising the steps of: melting (2) the steel and treating the steel in a ladle metallurgy installation (3); subsequently continuously casting the steel (4) into a thin slab (5 a) in a continuous casting mold (14), partially deforming, cutting the slab into partial strand lengths (15), descaling (28), heating to rolling temperature and homogenizing in a soaking furnace (16), descaling again and rolling in a finishing mill (6 a), coiling in a first coiling station (20) immediately downstream of a last finishing stand (19) or, alternatively, downstream of a cooling line (21), and adjusting a final microstructure (9) in a cooling line (21) according to the desired grade of steel by cooling on a runout table (22), and finish-coiling the rolled product (1 a) in a second coiling station; wherein said step of melting the steel and treating the steel includes providing a system capable of carrying out a plurality of process routes for producing molten steel including the following routes: (a) producing the molten steel (1 b) in a melting installation (2 a) which is not a steelworks converter, and treating in a vacuum degassing system (27) and in a ladle furnace (25), and (b) melting in an electric arc furnace (2 b) or in a two vessel electric arc furnace, and treating in a ladle furnace (25) with an electrode system (31) and in a vacuum degassing system, and (c) melting in an electric arc furnace installation (35) or a two vessel electric arc furnace (30) capable of a two stage process or an individual furnace vessel (30), and treating in the ladle furnace (25) and in a differential-pressure vacuum degassing system (43), and (d) melting in an electric arc furnace (2 b) with additions of alloying materials (26), and treating by a partial-quantity degassing in the ladle furnace (25), or a vacuum degassing system (27) and a ladle degassing (27); and selecting a process route for producing the molten steel from the process routes (a) through (d) to achieve a desired final microstructure (9).
 2. Method in accordance with claim 1, wherein successive treatment steps (24) are carried out as a first process route (10) in the electric arc furnace (2 b) and in a ladle metallurgy installation (3) with at least one vacuum degassing system (27) followed by the ladle furnace (25) for decarbonization, reduction, and addition of alloying materials (26), and with the ladle furnace (25) for slag formation, for slag work, for temperature control, for final adjustment of a final analysis, and for purity rinsing to a desired Δ <Al> content.
 3. Method in accordance with claim 1, wherein successive treatment steps (24) are carried out as a second process route (11) in the electric arc furnace (2 b) or the electric arc furnace installation (35) and in a ladle metallurgy installation (3), with the ladle furnace (25) for slag formation for the heating and for the prereduction of the steel, with a vacuum degassing system (27) for the decarbonization and denitrogenation for the reduction of the slag on the steel surface for the desulfurization under reduced pressure, for a final adjustment of the final analysis and for the purity rinsing to a desired Δ <Al> under atmospheric pressure.
 4. Method in accordance with claim 1, wherein successive treatment steps (24) are carried out as a third process route (12) in the electric arc furnace (2 b) or in the electric arc furnace installation (35) and in a ladle metallurgy installation (3) with the ladle furnace (25) for temperature control and for prereduction with at least one differential-pressure degassing process (43) for the decarbonization, desulfurization and denitrogenation, reduction, and addition of alloying materials from an iron alloy, and with a final adjustment of the final analysis and for purity rinsing to <Al> contents <15 ppm bound aluminum (Al₂O₃).
 5. Method in accordance with claim 1, wherein successive treatment steps (24) are carried out as a fourth process route (13) in an electric arc furnace (2 b) or in an electric arc furnace installation (35) and in a ladle metallurgy installation (3) with a ladle furnace (25) for temperature control and a subsequent partial-quantity degassing (27 a) for decarbonization and denitrogenation, desulfurization, with a ladle degassing (27) for a final adjustment of the final analysis and for purity rinsing to desired Δ <Al> contents.
 6. Method in accordance with claim 1, wherein a descaling (28) is carried out directly below the continuous casting mold (14).
 7. Method in accordance with claim 1, wherein a controlled high-temperature oxidation (29) by a controlled atmosphere is carried out in the soaking furnace (16).
 8. Method in accordance with claim 1, wherein the partial strand lengths (15) are inductively heated downstream of the soaking furnace (16).
 9. Method in accordance with claim 1, wherein the partial strand lengths (15) are subjected to controlled cooling upstream of a first finishing stand (17) of the finishing mill (6 a).
 10. Method in accordance with claim 1, wherein continuous product (1 c) coiled in the second coiling station (23) is subjected to controlled cooling.
 11. Method in accordance with claim 1, wherein the electric arc furnace installation (35) comprises two furnace vessels (30), which are alternately operated with a swiveled electrode system (31) and an oppositely swiveled top injection lance (32), are operated with pig iron, direct reduced charge materials, and scrap, and are operated partially with electric power and/or chemical energy.
 12. Method in accordance with claim 1, wherein steels with multiphase microstructure are produced. 